New analysis of the causes of LED dead lights

　　LED dead lights are the key factor affecting product quality and reliability. How to reduce and eliminate dead lights and improve product quality and reliability are key issues that packaging and application companies need to solve.

　　The following is an analysis of some of the causes of dead lights: Static electricity damages the LED chip .

　　Static electricity damages LED chips, causing the PN junction of LED chips to fail, increasing leakage current and turning them into a resistor. Static electricity is a very harmful devil. Countless electronic components have been damaged by static electricity around the world, causing tens of millions of dollars in economic losses. Therefore, preventing static electricity from damaging electronic components is a very important task in the electronics industry. LED packaging and application companies must not take it lightly. Any problem in any link will cause damage to the LED, causing the LED performance to deteriorate or even fail. We know that the static electricity of the human body (ESD) can reach about 3,000 volts, which is enough to break down and damage the LED chip. In the LED packaging production line, it is also very important whether the grounding resistance of various equipment meets the requirements. Generally, the grounding resistance is required to be 4 ohms, and in some high-requirement occasions, the grounding resistance must even reach 2 ohms. These requirements are familiar to people in the electronics industry. The key is whether they are in place during actual implementation and whether there are records.

　　It is understood that in general private enterprises, anti-static measures are not in place, that is, most enterprises cannot find the test records of grounding resistance. Even if a grounding resistance test is done, it is only once a year, or once every few years, or the grounding resistance is checked when there is a problem. However, people do not know that grounding resistance testing is a very important task, at least 4 times a year (once every quarter). In some places with high requirements, a grounding resistance test is required every month.

　　Soil resistance varies with the seasons. In spring and summer, there is a lot of rain, so the wet soil grounding resistance is easier to reach. In autumn and winter, the dry soil has less moisture, and the grounding resistance may exceed the specified value. Recording is to save the original data so that it can be checked in the future. It complies with the ISO2000 quality management system. You can design a table for testing grounding resistance. Both packaging companies and LED application companies need to do grounding resistance testing. Just fill in the names of various equipment in the table, measure the grounding resistance of each device and record it, and the tester can sign and archive it.

　　Static electricity from the human body can also cause great damage to LEDs. When working, you should wear anti-static clothing and wear an anti-static ring. The anti-static ring should be well grounded. There is an anti-static ring that does not need to be grounded, but the anti-static effect is not good. It is recommended not to use this product. If the staff violates the operating procedures, they should receive corresponding warning education, which also serves as a warning to others. The amount of static electricity on the human body is related to the different fabrics of the clothes people wear and their physical constitution. When we take off our clothes in the dark night of autumn and winter, it is easy to see the discharge between the clothes. The voltage of this static discharge is 3,000 volts.

　　The ESD value of silicon carbide substrate chips is only 1100 volts, and the ESD value of sapphire substrate chips is even lower, only 500-600 volts. If we pick up a good chip or LED with our hands (without any protective measures), the result is predictable. The chip or LED will be damaged to varying degrees. Sometimes a good device breaks down inexplicably after passing through our hands. This is caused by static electricity.

　　If the packaging company does not strictly follow the grounding regulations, it will suffer the loss, which will cause the product qualification rate to drop and reduce the economic benefits of the company. Similarly, if the equipment and personnel of the company using LED are not grounded properly, it will also cause damage to the LED, and rework is inevitable. According to the requirements of the LED standard manual, the lead of the LED should be no less than 3-5 mm away from the colloid for bending or welding, but most application companies do not do this, and only directly weld with a thickness of a PCB board (2 mm) apart, which will also cause damage or damage to the LED, because the excessively high welding temperature will affect the chip, which will deteriorate the chip characteristics, reduce the luminous efficiency, and even damage the LED. This phenomenon is common.

　　Some small businesses use manual soldering and use a 40-watt ordinary soldering iron. The soldering temperature cannot be controlled and the soldering iron temperature is above 300-400°C. Excessively high soldering temperature can also cause dead lights. The expansion coefficient of LED leads at high temperatures is several times higher than the expansion coefficient at around 150°C. The internal gold wire solder joints will be pulled apart due to excessive thermal expansion and contraction, causing dead lights.

　　Analysis of the reasons for the LED lamp dead light phenomenon caused by open circuit of internal connection solder joints

　　The direct cause of LED dead lights is the incomplete production process of packaging enterprises and backward inspection methods for incoming materials. Generally, LEDs are packaged with brackets, which are made of copper or iron metal materials and stamped by precision molds. Since copper is expensive, the cost is naturally high. Influenced by fierce market competition, in order to reduce manufacturing costs, most of the market uses cold-rolled low-carbon steel to stamp LED brackets , and iron brackets must be silver-plated.

　　Silver plating has two functions, one is to prevent oxidation and rust, the other is to facilitate welding. The electroplating quality of the bracket row is very critical, it is related to the life of the LED, the treatment before electroplating should be carried out strictly according to the operating procedures, rust removal, degreasing, phosphating and other processes should be meticulous, the current should be controlled during electroplating, the thickness of the silver plating layer should be controlled, too thick plating will cost a lot, too thin will affect the quality. Because general LED packaging companies do not have the ability to inspect the electroplating quality of the bracket row, this gives some electroplating companies an opportunity to make the silver plating layer of the electroplated bracket row thinner and reduce cost expenditure. General packaging companies lack IQC inspection means for the bracket row, and there is no instrument to detect the thickness and fastness of the bracket row plating layer, so it is easier to get away with it.

　　I have seen some brackets rust after being placed in the warehouse for a few months. Not to mention being used, it shows how poor the quality of electroplating is. Products made with such brackets will definitely not last long. Not to mention 30,000-50,000 hours, even 10,000 hours will be a problem. The reason is very simple. There is a period of south wind every year. In such weather, the air is humid, which can easily cause poorly plated metal parts to rust and make LED components ineffective. Even if the LED is packaged, the silver coating is too thin and the adhesion is not strong, and the solder joints are separated from the bracket, resulting in a dead light phenomenon. This is what we encounter when the lamp that was used well does not light up. In fact, the internal solder joints are separated from the bracket.

　　Each process in the packaging process must be carefully operated. Any negligence in any link will cause the dead light. In the soldering and die bonding process, too much or too little silver glue (for single solder joint chips) will not work. Too much glue will return to the chip gold pad, causing a short circuit, and too little will make the chip not stick firmly. The same is true for the double solder joint chip. Too much insulating glue will return to the chip gold pad, causing a cold solder joint during welding and thus a dead light.

　　If there are too few dots, the chip will not stick firmly, so the glue must be dispensed just right, neither too much nor too little. The welding process is also critical. The four parameters of the gold wire ball welder, pressure, time, temperature, and power, must be coordinated just right. Except for the fixed time, the other three parameters are adjustable. The pressure should be adjusted moderately. Too much pressure can easily crush the chip, and too little pressure can easily cause cold soldering. The welding temperature is generally adjusted to 280°C. The power adjustment refers to the ultrasonic power adjustment. Too much or too little is not good. Moderate is the best. In short, the adjustment of various parameters of the gold wire ball welder is to use the welded material and use a spring torque tester to test 6 grams, which is qualified.

　　Every year, the parameters of the gold wire ball welding machine are tested and calibrated to ensure that the welding parameters are in the best state. In addition, there are also requirements for the arc of the welding wire. The arc height of the single-solder chip is 1.5-2 chip thicknesses, and the arc height of the double-solder chip is 2-3 chip thicknesses. The height of the arc will also cause quality problems of the LED. If the arc height is too low, it is easy to cause the dead light phenomenon during welding, and if the arc height is too high, the resistance to current shock is poor.

　　LED dead light caused by cold soldering. How to identify cold soldering dead light: Use a lighter to heat the LED lead wire to 200-300℃, remove the lighter, and connect the LED with a 3V button battery according to the positive and negative poles. If the LED light can light up at this time, but as the lead wire temperature decreases, the LED light changes from bright to dark, which proves that the LED light is cold soldered. The reason why heating can light up is that it uses the principle of metal thermal expansion and contraction. When the LED lead wire is heated, it expands and stretches to connect with the internal solder joint. At this time, the power is turned on and the LED can emit light normally. As the temperature drops, the LED lead wire shrinks and returns to the normal temperature state, disconnecting from the internal solder joint, and the LED light will not light up. This method has been tried and tested many times and is effective.

　　Solder the two leads of the dead light with cold solder joints to a metal bar, soak it in concentrated sulfuric acid to dissolve the colloid on the outside of the LED, take it out after the colloid is completely dissolved, and observe the welding conditions of each soldering point under a magnifying glass or microscope. This way, you can find out whether the problem is with the first or second soldering, whether the parameters of the gold wire ball soldering machine are set incorrectly, or other reasons, so as to improve the method and process to prevent the cold solder joint phenomenon from happening again.

　　However, even in the exhibits at the China Electronics Show, users who use LED products will encounter the phenomenon of dead lights. This is the phenomenon of dead lights after using LED products for a period of time. There are two reasons for dead lights. Open circuit dead lights are caused by poor welding quality or problems with the quality of bracket electroplating. The increase in LED chip leakage current will also cause the LED light to not light up. In order to reduce costs, many LED products now do not have anti-static protection, so it is easy for the chip to be damaged by induced static electricity. Thunderstorms on rainy days are prone to induced high-voltage static electricity in the power supply line, and spike pulses superimposed on the power supply line, which will cause LED products to suffer varying degrees of damage.

　　In short, there are many reasons for dead lights, which cannot be listed one by one. Dead lights may occur in every link from packaging, application, to use. How to improve the quality of LED products is an issue that packaging companies and application companies should attach great importance to and seriously study. From chip and bracket selection to LED packaging, the entire process should be operated in accordance with the ISO2000 quality system. Only in this way can the quality of LED products be comprehensively improved, and long life and high reliability can be achieved. In the circuit design of the application, choosing varistors and PPTC components to improve the protection circuit, increase the number of parallel paths, use constant current switching power supplies, and add temperature protection are all effective measures to improve the reliability of LED products. As long as the packaging and application companies operate strictly in accordance with the ISO2000 quality system, the quality of LED products will definitely be taken to a new level.