CMCW2012F220KTT
CUSTOMER：
CUSTOMER P/N:
Cybermax P/N:
DRAWN NO.:
CMCW2012F220KTT
CM190705001
PAGE：
REVISION：
DATE：
2/10
19.07.05
Reliability Test
No.
1
Item
Temperature Shock.
Specification
Appearance: No damage.
Inductance: within ±10% of
initial.
Appearance: No damage.
Test Method
Temperature: -25±2℃~+105±2℃ Kept for 30 minutes.
Transition time : 5 minutes.
100 Cycles.
Temperature: 40±2℃.
Relative Humidity: 90%.
Duration: 500 +4/-0 hours.
Temperature: 105±2℃.
Duration: 1000 +4/-0 hours.
2
Humidity Resistance.
Inductance: within ±10% of
initial.
3
High Temperature
Resistance.
Appearance: No damage.
Inductance: within ±10% of
initial.
Appearance: No damage.
Inductance: within ±10% of
initial.
Appearance: No damage.
4
Low Temperature
Resistance.
Temperature: -25±2℃.
Duration: 1000 +4/-0 hours.
Oscillation Frequency: 10Hz to 55Hz to 10Hz in 60 seconds
as a period. Total amplitude: 1.5mm.
Testing Time: a period of 2 hours in each 3 mutually
perpendicular directions (total of 6 hours).
Solder temperature: 260 +0/-5℃. Duration: 5 sec.
Allowed reflow time: 2 times.
Preheating: 160℃,60sec.
Solder temperature: 245±5℃.
Duration : 5 sec.
Flexure: 2mm.
5
Vibration test.
Inductance: within ±10% of
initial.
Appearance: No damage.
6
Solderability Heat test. Inductance: within ±10% of
initial.
90% or more of electrode area
shall be coated by new solder.
7
Solderability test.
8
Flexure Strength.
No visible mechanical damage. Pressurizing Speed: 0.5mm/sec.
Keep time: 30±1sec.
Force: 0.45Kg for 0603 series. Force: 0.9Kg for 0805
9
Terminal Strength.
No visible mechanical damage. series. Force: 1.8Kg for 1008 series above.
Keep time: 5 sec，X,Y directs.
Rev.01
Page 4 of 11
www.cybermaxtech.com