SPECIFICATION
Supplier : Samsung electro-mechanics
Product : Multi-layer Ceramic Capacitor
A. Samsung Part Number
CL
①
①
Series
②
Size
③
Dielectric
④
Capacitance
⑤
Capacitance
tolerance
⑥
Rated Voltage
⑦
Thickness
16 V
1.25 ± 0.15 mm
31
②
B
③
105
④
K
⑤
O
⑥
F
⑦
N
⑧
N
⑨
N
⑩
F
⑪
Samsung P/N :
CL31B105KOFNNNF
Description :
CAP, 1㎌, 16V, ±10%, X7R, 1206
Samsung Multi-layer Ceramic Capacitor
1206 (inch code)
X7R
1
㎌
±10 %
L: 3.2 ± 0.15
mm
W:
1.6
Ni
Cu
Sn 100%
Normal
Reserved for future use
Embossed Type,13"reel
(10,000ea)
(Pb Free)
± 0.15 mm
⑧
Inner electrode
Termination
Plating
⑨
Product
⑩
Special
⑪
Packaging
B. Samsung Reliability Test and Judgement condition
Performance
Capacitance
Tan
δ
(DF)
Insulation
Resistance
Appearance
Withstanding
Voltage
Temperature
Characteristics
Adhesive Strength
of Termination
Bending Strength
Solderability
No abnormal exterior appearance
No dielectric breakdown or
mechanical breakdown
X7R
(From -55℃ to 125℃, Capacitance change should be within ±15%)
No peeling shall occur on the
500gF, for 10±1 sec.
terminal electrode
Capacitance change :
within ±12.5%
Bending to the limit (1mm)
with 1.0mm/sec.
More than 75% of terminal surface
is to be soldered newly
SnAg3.0Cu0.5 solder
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to
Soldering heat
Capacitance change :
Tan
δ,
IR : initial spec.
within ±7.5%
Solder pot : 270±5℃, 10±1sec.
Visual inspection
250% of the rated voltage
Within specified tolerance
0.035 max.
More than 100Mohm㎌
Rated Voltage
60~120 sec.
1㎑±10%
Test condition
1.0±0.2Vrms
Performance
Vibration Test
Capacitance change :
Tan
δ,
IR : initial spec.
Moisture
Resistance
Capacitance change :
Tan
δ
: 0.05 max
IR
High Temperature
Resistance
: More than 25㏁·㎌
within ±12.5%
With 200%
within ±12.5%
within ±5%
Test condition
Amplitude : 1.5mm
From 10㎐ to 55㎐ (return : 1min.)
2hours
3 direction (x, y, z)
With rated voltage
40±2℃, 90~95%RH, 500+12/-0 hours
Capacitance change :
Tan
δ
: 0.05 max
IR
of the rated voltage
Max. operating temperature
1000+48/-0 hours
: More than 50㏁·㎌
within ±7.5%
1 cycle condition
Min. operating temperature
→
→
25℃
25℃
Max. operating temperature
→
Temperature
Cycling
Capacitance change :
Tan
δ,
IR : initial spec.
5 cycles test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For more detailed Specification, Please refer to the Samsung MLCC catalogue.