Monolithic structure for closed magnetic path eliminates
crosstalk and provides high reliability in a wide range
of temperature and humidity ranges
■
Standard EIA packages: 1J, 2A, 2B
■
Nickel barrier with solder overcoa
for excellent solderability
■
Magnetically shielded
2. 2.1 Dimensions
L
W
Solder
Plating
Ni
Plating
Silver
Metallization
d
Size
Code
1J
(0603)
2A
(0805)
2B
(1206)
L
.063±.006
(1.6±0.15)
.079±.008
(2.0±0.2)
.126±.008
(3.2±0.2)
W
.031±.006
(0.8±0.15)
.049±.008
(1.25±0.2)
.063±.008
(1.6±0.2)
t
.031±.006
(0.8±0.15)
.035±.008
(0.9±0.2)
.043±.008
(1.1±0.2)
t
Terminations
(Metallization
Bands)
d
Electrodes
3. Ordering and Specifying Information*
MCL
Type
1J
Size
1J
2A
2B
H
Material
Permeability
Code:
H
J
T
Termination
Material
T: Sn
(Other termination
styles available,
contact factory
for options)
TE
Packaging
TD: 7" Paper Tape
(1J - 4,000 pcs/reel; 2A - 0.047µH
- 2.2µH = 4,000 pcs/reel)
TE: 7" Embossed Plastic
(2A - 2.7µH - 10µH = 3,000
pcs/reel; 2B - 3,000 pcs/reel)
R10
Nominal
Inductance
047 = .047µH
R10 = .100µH
* Please note: KSE’s part numbers do not contain any spaces or hyphens.
4. Standard Applications
Part
Designation
MCL1JHTTD047M
MCL1JHTTD068M
MCL1JHTTD082M
MCL1JHTTDR10*
MCL1JHTTDR12*
MCL1JHTTDR15*
MCL1JHTTDR18*
MCL1JHTTDR22*
MCL1JHTTDR27*
Inductance
L (µH)
0.047
0.068
0.082
0.10
0.12
0.15
0.18
0.22
0.27
Minimum
Q
L.Q. Test
Frequency
(MHz)
50
Self Resonant
Frequency
Typical
(MHz)
260
250
245
240
205
180
165
150
136
DC
Resistance
Maximum
(Ω)
0.30
Allowable
DC Current
Maximum
(mA)
10
0.50
0.60
0.80
50
15
25
* Add tolerance character (K, M) - Other tolerances available upon request
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www
Spec ific ation s g iven herein m ay be cha nged a t any tim e w itho ut pr ior not ice. Pleas e c onf ir m te chnic al s pec if ica tions before you
MCL1JHTTDR33*
MCL1JHTTDR39*
MCL1JHTTDR47*
MCL1JHTTDR56*
MCL1JHTTDR68*
MCL1JHTTDR82*
MCL1JJTTD1R0*
MCL1JJTTD1R2*
MCL1JJTTD1R5*
MCL1JJTTD1R8*
MCL1JJTTD2R2*
MCL1JJTTD2R7*
MCL1JJTTD3R3*
MCL1JJTTD3R9*
MCL1JJTTD4R7*
MCL1JJTTD5R6*
MCL1JJTTD6R8*
MCL1JJTTD8R2*
MCL1JJTTD100*
MCL1JJTTD120*
MCL2AHTTD047M
MCL2AHTTD068M
MCL2AHTTD082M
MCL2AHTTDR10*
MCL2AHTTDR12*
MCL2AHTTDR15*
MCL2AHTTDR18*
MCL2AHTTDR22*
MCL2AHTTDR27*
MCL2AHTTDR33*
MCL2AHTTDR39*
MCL2AHTTDR47*
MCL2AHTTDR56*
MCL2AHTTDR68*
MCL2AHTTDR82*
MCL2AJTTD1R0*
MCL2AJTTD1R2*
MCL2AJTTD1R5*
MCL2AJTTD1R8*
MCL2AJTTD2R2*
MCL2AJTTE2R7*
MCL2AJTTE3R3*
MCL2AJTTE3R9*
MCL2AJTTE4R7*
0.33
0.39
0.47
0.56
0.68
0.82
1.0
1.2
1.5
1.8
2.2
2.7
3.3
3.9
4.7
5.6
6.8
8.2
10
12
0.047
0.068
0.082
0.10
0.12
0.15
0.18
0.22
0.27
0.33
0.39
0.47
0.56
0.68
0.82
1.0
1.2
1.5
1.8
2.2
2.7
3.3
3.9
4.7
15
25
10
35
4
30
2
15
50
20
25
25
45
10
125
110
105
95
90
85
75
65
60
55
50
45
40
35
33
22
20
18
17
15
320
280
255
235
220
200
185
170
150
145
135
125
115
105
100
75
65
60
55
50
45
41
38
35
0.85
1.00
1.35
1.55
1.70
2.10
0.60
0.80
0.95
1.15
1.35
1.55
1.70
2.10
1.55
1.70
2.10
1.85
2.10
0.20
35
25
15
5
3
300
0.30
0.40
0.50
0.55
0.65
0.75
0.80
1.00
0.40
0.50
0.60
0.65
0.75
0.80
0.90
1.00
200
250
150
50
30
* Add tolerance character (K, M) - Other tolerances available upon request
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www
Spec ific ation s g iven herein m ay be cha nged a t any tim e w itho ut pr ior not ice. Pleas e c onf ir m te chnic al s pec if ica tions before you
MCL2AJTTE5R6*
MCL2AJTTE6R8*
MCL2AJTTE8R2*
MCL2AJTTE100*
MCL2BHTTE047M
MCL2BHTTE068M
MCL2BHTTER10*
MCL2BHTTER12*
MCL2BHTTER15*
MCL2BHTTER18*
MCL2BHTTER22*
MCL2BHTTER27*
MCL2BHTTER33*
MCL2BHTTER39*
MCL2BHTTER47*
MCL2BHTTER56*
MCL2BHTTER68*
MCL2BHTTER82*
MCL2BJTTE1R0*
MCL2BJTTE1R2*
MCL2BJTTE1R5*
MCL2BJTTE1R8*
MCL2BJTTE2R2*
MCL2BJTTE2R7*
MCL2BJTTE3R3*
MCL2BJTTE3R9*
MCL2BJTTE4R7*
MCL2BJTTE5R6*
MCL2BJTTE6R8*
MCL2BJTTE8R2*
MCL2BJTTE100*
MCL2BJTTE120*
MCL2BJTTE150*
MCL2BJTTE180*
MCL2BJTTE220*
MCL2BJTTE270*
MCL2BJTTE330*
5.6
6.8
8.2
10
0.047
0.068
0.10
0.12
0.15
0.18
0.22
0.27
0.33
0.39
0.47
0.56
0.68
0.82
1.0
1.2
1.5
1.8
2.2
2.7
3.3
3.9
4.7
5.6
6.8
8.2
10
12
15
18
22
27
33
50
4
2
50
20
25
25
45
10
4
50
2
32
29
26
24
320
280
235
220
200
185
170
150
145
135
125
115
105
100
75
65
60
55
50
45
41
38
35
32
29
26
24
22
19
18
16
14
13
0.90
1.00
1.10
1.15
0.15
0.25
0.30
0.40
0.50
0.60
0.50
0.60
0.70
0.80
0.90
0.40
0.50
15
300
250
200
150
100
0.60
50
0.70
0.80
0.85
0.90
1.00
1.05
0.70
0.90
1.05
5
25
15
30
1
0.4
* Add tolerance character (K, M) - Other tolerances available upon request
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www
Spe cific at io ns g ive n herein m ay be ch anged a t any tim e w ith out p rior not ice. Pleas e c onf ir m t echn ic al s pec ifica tions before you
Storage Temperature
40°C @ 70% Humidity
Sealed plastic bags with desiccan
used to reduce the potential of ox
the terminations during storage.
Flux:
5-10 sec dip
After Flux:
Air dry for 15 sec
Preheat:
150°C ±10°C
Preheat Time:
60 sec
Solder Temp:
260°C ±5°C
Dip Time:
10 ±1 sec
Flux:
5-10 sec dip
After Flux:
Air dry for 15 sec
Solder Temp:
245°C ±5°C
Dip Time:
5 ±0.5 sec
Resistance to Solder
Heat
Change in Inductance:
Relative to value before
test ±20%.
Appearance:
There shall be no cracking
Solder Coverage:
More than 75% of the terminal
electrode shall be covered with solder.
Solder Coverage:
More than 95% of the
termination shall be covered with solder.
Solderability
Leach Resistance
Appearance:
There shall be no visible signs of
physical or mechanical damage (i.e. no cracks)
Terminations:
Termination must not be leached
away for more than 5%.
The bead shall be subjected to th
5 steps for the period of time show
The 5 steps constitute one (1) rot
4 rotations shall be carried out.
1) Flux:
5-10 sec
2) After Flux:
Air dry for 15 sec
3) Solder Temp:
230°C ±5°C
4) Dip Time:
5 ±0.5 sec
5) Cool:
Air cool for 60 seconds
Insulation Resistance
Solvent Resistance
Insulation Resistance:
Min 1G ohms
Change in Inductance:
Relative to value before
test ±10%.
Cleaning by:
Washer:
Ultrasonic washer (100W
Solvent:
Isopropyl alcohol
Time:
3 minutes
Type
1J (0603)
2A (0805)
2B (1206)
Type
1J (0603)
2A (0805)
2B (1206)
W(kgf)
0.5
1.0
1.5
W(kgf)
1.4
1.8
2.3
30
30
30
Terminal Strength
(hanging test)
Appearance:
The terminal electrode shall not
break off, nor shall there be damage to the body.
Terminal Strength
(push test)
Appearance:
There shall be no evidence of
mechanical degradations to terminals or body.
Bending Strength
Appearance:
There shall be no physical or
mechanical damage
Inductance:
Relative to initial value before
test ±10%
Board:
90x40x1.6mm
Bend:
1mm
Time:
5 sec
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www
Spec ific ation s g iven herein m ay be cha nged a t any tim e w itho ut pr ior not ice. Pleas e c onf ir m te chnic al s pec if ica tions before you
mechanical damage
Inductance:
Relative to initial value before test
±10%
Vibration
Inductance:
Relative to initial value ±10%
Time:
11 msec
There shall be 3 shocks in each o
(18 shocks total).
Only endurance conditioning by s
be made. The entire frequency ra
10-2,000 Hz and return to 10 Hz
(this shall constitute one cycle).
Amplitude: 1.5mm
The test shall have a 15G peak a
applied for a period of 4 hours (12
in each of 3 mutually perpendicul
(a total of 36 cycles within a total
Step
1-start
2-hold
3-transfer
4-hold
5-transfer
Temperature
-40°C ±2°C
-40°C ±2°C
—
+105°C ±2°C
—
Thermal Shock
Appearance:
There shall be no physical or
mechanical damage.
Inductance:
Relative to initial value ±20%.
DCR:
The DCR shall not exceed initial specified
value.
Testing of the parts will be made at 0 hours, 250
hours and 500 hours. Before testing the parts
shall be allowed to cool to room temperature for
24 hours.
30
0.5
30
0.5
Steps 1 thru 5 constitute one com
cycle and the test shall consist of
of 500 cycles.
Temperature:
85°C ±2°C
Relative Humidity:
85%
Time:
1,000 hours total
Apply:
100% rated current
Load Humidity
Appearance:
There shall be no physical or
mechanical damage
Inductance:
Relative to initial value ±15%
Measurements shall be taken at 0 hours, 250
hours, 500 hours and 1,000 hours and shall meet
the conditions stated above.
Life Test
Appearance:
There shall be no physical or
mechanical damage
Inductance:
Relative to initial value ±15%
Measurements shall be taken at 0 hours, 250
hours, 500 hours and 1,000 hours and shall meet
the conditions stated above.
Temperature:
85°C ±2°C
Time:
1,000 hours total
Apply:
100% rated current
6. Packaging Specifications
KOA’s multi layer components are provided on tape-and-reel
for use in pick-and-place machines. The reel size is 7 inch.
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www
Spec ific ation s g iven herein m ay be cha nged a t any tim e w itho ut pr ior not ice. Pleas e c onf ir m te chnic al s pec if ica tions before you
京公网安备 11010802033920号
EEWORLD